The result of 3 temperature levels of two action warmth treatment method system on microstructure and mechanical house of around β Ti-5Al-5Mo 5V-lCr- IFe (TC18) titanium alloy was investigated systematically. The experiment effects confirmed that Together with the expanding of lower-phase temperature, the amount fraction and sliape of Principal